| PC PC-110 臺(tái)灣奇美實(shí)業(yè)股份有限公司 物性數(shù)據(jù) |
| 規(guī)格級(jí)別： | --- | 外觀顏色： | --- |
| 用途概述： | 嬰兒奶瓶、汽車警示燈亮、鼠標(biāo)、巧克力盛裝盒、高跟鞋、安全鏡片等。 | ||
| 備注說(shuō)明： | 特性：一般射出成型用 | ||
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |||||||||||
| 基本性能 | 熔體流動(dòng)速率 | 300℃，1.2kg | ASTM D-1238 | 10 | g/10min | ||||||||||
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.20 | % | |||||||||||
| 物理性能 | 全光穿透率 | 3mmt | ASTM D-570 | 89 | % | ||||||||||
| 比重 | 23/23℃ | ASTM D-792 | 1.20 | --- | |||||||||||
| 濁度 | 3.2mmt | ASTM D-1003 | ＜0.8 | % | |||||||||||
| 機(jī)械性能 | 曲折率 | --- | ASTM D-542 | 1.585 | % | ||||||||||
| 降伏引張強(qiáng)度 | 23℃ | ASTM D-638 | 630 | kg/m2 | |||||||||||
|
|
|
|
|
|||||||||||
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790 | 920 | kg/m2 | |||||||||||
| 彎曲模數(shù) | 23℃ | ASTM D-790 | 24000 | kg/m2 | |||||||||||
| IZOD缺口沖擊強(qiáng)度 | 1/4" | ASTM D-256 | 14.3 | kg.cm/cm | |||||||||||
| IZOD缺口沖擊強(qiáng)度 | 1/8" | ASTM D-256 | 87 | kg.cm/cm | |||||||||||
| 洛氏硬度 | --- | ASTM D-785 | M-77 | M Scale | |||||||||||
| 壓縮強(qiáng)度 | --- | ASTM D-695 | 780 | Kg/cm2 | |||||||||||
| 電氣性能 | 體積電阻率 | --- | ASTM D-257 | 3 | ×1016Ω.cm | ||||||||||
| 介電常數(shù) | 60Hz | ASTM D-150 | 2.95 | --- | |||||||||||
| 介電常數(shù) | 106Hz | ASTM D-150 | 2.9 | --- | |||||||||||
| 介電損耗 | 60Hz | ASTM D-150 | 0.0004 | --- | |||||||||||
| 介電損耗 | 106Hz | ASTM D-150 | 0.009 | --- | |||||||||||
| 絕緣破壞強(qiáng)度 | 1.6mm | ASTM D-149 | 30 | KV/mm | |||||||||||
| 耐電弧性 | --- | ASTM D-495 | 110 | Sec | |||||||||||
| 加工性能 | 成型收縮率 | Across | ASTM D-955 | 0.5-0.7 | % | ||||||||||
| 成型收縮率 | Parallel | ASTM D-955 | 0.5-0.7 | % | |||||||||||
| 熱 性 能 | 熱傳導(dǎo)系數(shù) | --- | ASTM C-177 | 0.2 | W/m℃ | ||||||||||
| 維卡軟化點(diǎn) | 1Kg,50℃/hr | ASTM D-1525 | 153 | ℃ | |||||||||||
| 線膨脹系數(shù) | 40～100℃ | ASTM D-696 | 6-8 | ×10-5cm/cm/℃ | |||||||||||
| 燃燒性 | 1/16" | UL 94 | V-2 | --- | |||||||||||
| 熱變形溫度 | 未退火,4.6Kg/cm2,120℃ | ASTM D-648 | 136 | ℃ | |||||||||||
| 熱變形溫度 | 未退火,18.6Kg/cm2,120℃ | ASTM D-648 | 125 | ℃ | |||||||||||